Brand: SheraInvestment for crown and bridge technique
~ Premium quality for gold, gold telescopics, non-precious alloys and pressable ceramics
~ Very fine with a dense consistency for castings, the expansion is easy to control with results having a very smooth surface and exceptional precise fit
~ Used for shock heat process and the traditional slow heating process -
Brand: Shera
Investment for crown and bridge technique
~ Premium quality for gold, gold telescopics, non-precious alloys and pressable ceramics
~ Very fine with a dense consistency for castings, the expansion is easy to control with results having a very smooth surface and exceptional precise fit
~ Used for shock heat process and the traditional slow heating process -
Brand: Shera~ special expansion liquid for all SHERA investments
~ can be mixed with distilled water according to the recommendations given for the investment used
~ sensitive to cold
-
Brand: SheraCyano-acrylate adhesive. Low viscosity anaerobic super glue in a specially designed bottle with non-blocking tip. Exceptional resistance to high and low temperatures. Instant adhesive based on cyanoacrylate ~ Viscosity: 20-40 mPas ~ Excellent adhesive strength ~ High fluidity ~ Patented lid ~ Anaerobic instant adhesive
-
Brand: SheraSuper hard stones for especially high demands
~ For implant works, for sectioned, master and static models
~ Good thixotrope quality and very good flow characteristics
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Exceptional hardnessTechnical specification
mixing ratio (powder : distilled water) 100 : 20 hardness after 2 h (MPa; N/mm2) 310 hardness after 24 h (MPa; N/mm2) 340 compressive strength after 1 h (MPa; N/mm2) 64 compressive strength after 1 h (psi) 9,280 setting expansion after 2 h (%) 0.10 working time (min) 6.0 – 7.0 end of setting (min) approx. 30 -
Brand: Shera
Super hard stones for especially high demands
~ For implant works, for sectioned, master and static models
~ Good thixotrope quality and very good flow characteristics
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Exceptional hardnessTechnical specification
mixing ratio (powder : distilled water) 100 : 20 hardness after 2 h (MPa; N/mm2) 310 hardness after 24 h (MPa; N/mm2) 340 compressive strength after 1 h (MPa; N/mm2) 64 compressive strength after 1 h (psi) 9,280 setting expansion after 2 h (%) 0.10 working time (min) 6.0 – 7.0 end of setting (min) approx. 30