Brand: DentaurumDentaurum Rematitan, Ti5 Milling Blank
- For high demands.
- Titanium alloy (Ti Al 6 V4) with increased mechanical hardness.
- Particularly suitable for long-span, delicate framework structures and for implant work
Product sizes available
10mm, 12mm, 15mm, 20mm, 25mm, 30mm
Product advantages:
- High mechanical strength.
- High biocompatibility in implant quality.
- Ideal for ceramic veneering using bonding ceramics suitable for titanium such as ceraMotion® Ti.
- High degree of corrosion resistance.
-
Brand: EisenbacherNPM Cobalt-based dental milling alloy for metal-ceramic, type 4, with step / shoulder
- Optimised milling properties due to special heat treatment
- High strength due to homogeneous metal structure
- Suitable for all high fusing veneering ceramics
Indications:
- Crowns and bridges for metal-ceramics
- Superstructures and bars
Technical Parameters:
- Yield Strength MPa – 440
- Elongation (%) – 14
- GPa – 210
- Tensile Strength – 819
- Density (g/cm3) – 8.55
- Hardness (HV 10/30) – 275
-
Brand: EisenbacherTitan based dental milling alloy for metal-ceramics, with step / shoulder.
- Clinical approved titanium alloy with high strength
- Very good milling properties
- Suitable for veneering with Ti-ceramics
Indications:
- Crowns and bridges for metal-ceramics
- Superstructures and bars
Technical Properties:
- Yield Strength (MPa) – 816
- Elongation (%) – 15
- Youngs Modul (GPa) – 115
- Tensile Strength (MPa) – 885
- Density (g/cm3) – 4.4
- Hardness (HV 10/30) – 318
-
Brand: UpceraResidue free burn + easy milling without deformation.
Technical Parameters
- Melting Point – 110c-115c
- Hardness – 45-55
- Thermal Expansion – 5%
- Diameter – 98mm
-
Brand: UpceraUpcera Explore Function Zirconia, with gradient translucency (43% – 46.6%) and strength (1300MPa – 1027MPa).
Available in thickness 12, 14, 16, 18, 20, 22 and 25mm.
Available in shades A1-BL4.
-
Brand: UpceraFLNT Base is a PMMA disk, characterized by high impact resistance. It is designed for CAD/CAM fabrication of denture bases with exceptional
color matching to oral gingival tissues.When combined with FLNT Temp Multi-layer, it enables the flawless production of complete full dentures.
Sizes Available:
25mm, 30mm & 35mm
Standard Colours Available:
Pink, Light Pink, Dark Pink, Light Reddish Pink, Opaque Pink
Aesthetic Colours Available – V (Veined):
V-Pink, V-Light Pink, V-Dark Pink, V-Light Reddish Pink, V-Opaque Pink
Ultimate Flexural Strength – >90MPa
Flexural Modulus – ≥2000MPa
Dissolution Value – ≤1.6µg/mm3
Residual monomer content – ≤2.2%
Water Absorbtion Rate – ≤32µg/mm3
-
Brand: UpceraFLNT Temp is a cross-linked PMMA disc designed for CAD/CAM fabrication of temporaries.
It exhibits high material homogeneity with no polymerization shrinkage or inhibition.
Owing to its superior material properties, including high fracture strength, this product offers broad clinical applicability.Sizes Available:
D98: 20mm, 25mm, 30mm + 35mm
Shades Available:
A1 – BL4
Flexural Strength – 135.7MPa
Vickers hardness – 21.56
Dissolution Value – ≤7.5µg/mm3
Density – 1.188g/cm3
Water Absorbtion Rate – ≤40µg/mm3