Good adhesive strength, suitable for plasters, metals and resins.
~ Model cement
~ 70g
~ 12 Sticks
~ Colour: Ivory
Good adhesive strength, suitable for plasters, metals and resins.
~ Model cement
~ 500g
~ 80 Sticks
~ Colour: Ivory
~ 20 x 0.25 mm
~ For ceramic
~ Glass-fibre reinforced
~ High cutting performance
~ 10 Pack
~ Max speed ↻ 50,000 RPM
Catalyst for Shera silicone putties
~ In plastic tube
~ Simple to dose
Super hard stones for especially high demands
~ For implant works, for sectioned, master and static models
~ Good thixotrope quality and very good flow characteristics
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Exceptional hardness
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 310 |
hardness after 24 h (MPa; N/mm2) | 340 |
compressive strength after 1 h (MPa; N/mm2) | 64 |
compressive strength after 1 h (psi) | 9,280 |
setting expansion after 2 h (%) | 0.10 |
working time (min) | 6.0 – 7.0 |
end of setting (min) | approx. 30 |
The grinding and polishing material in DiaDisc is diamond. This hardest mineral on earth is accurately sieved.
Thus the diamond size distribution in the DiaDisc is very narrow.
The ceramic bonded DiaDiscs show a very precise true running, a long lifetime and a very effective grinding performance.
The very thin DiaDiscs are distinguished by high flexibility and metal free bonding. The dental materials zirconium oxide, dental ceramic and veneer composite are easily ground with DiaDisc.
Cotton and silicone buff ideal for polishing acrylics, Valplast & Thermosens.
Fibre reinforced
~ 22 x 0.3 mm
~ For non-precious metal, gold and ceramic
~ Very flexible
~ Extreme long service life
~ 20 Pack
~ Max speed ↻ 35,000 RPM
Duplicating silicone
~ Colour: blue
~ Shore hardness A 17
~ Soft and elastic
~ Setting time: 20 minutes
~ Even for models with undercut thin dies
~ Yields to the expansion of the investment
Super hard stones for especially high demands
~ For implant works, for sectioned, master and static models
~ Good thixotrope quality and very good flow characteristics
~ Can be scanned with several systems
~ Ideal for plastic basing systems
~ Exceptional hardness
Technical specification
mixing ratio (powder : distilled water) | 100 : 20 |
hardness after 2 h (MPa; N/mm2) | 310 |
hardness after 24 h (MPa; N/mm2) | 340 |
compressive strength after 1 h (MPa; N/mm2) | 64 |
compressive strength after 1 h (psi) | 9,280 |
setting expansion after 2 h (%) | 0.10 |
working time (min) | 6.0 – 7.0 |
end of setting (min) | approx. 30 |
Cotton and silicone buff ideal for polishing chrome.